|TEMPERATURE-DEPENDENT MAGNETIC PROPERTIES OF ELECTRODEPOSITED COPTP ALLOY NANOWIRES|
|Cite This Article:|
TEMPERATURE-DEPENDENT MAGNETIC PROPERTIES OF ELECTRODEPOSITED COPTP ALLOY NANOWIRES, International Journal of Innovative Research in Technology(www.ijirt.org) ,ISSN: 2349-6002 ,Volume 5 ,Issue 4 ,Page(s):307-310 ,September 2018 ,Available :IJIRT147135_PAPER.pdf
|CoPtP alloy Magnetic nanowires • Coercivity • Electrodeposition • Alumina template|
|CoPtP alloy nanowires,~200 nm in diameter, have been prepared by the electrodeposition method into the pores of a porous anodic aluminum oxide template. X-ray diffraction pattern shows that the wires consist of a mixture of fcc and hcp phases with CoPt (002) and CoPt (221) texture. The coercivity was found to be 1150 Oe at 50 K and 760 Oe at 300 K, when the field was applied parallel to the wire axis. The temperature dependence of coercivity was explained by considering the magnetocrystalline anisotropy and thermal activation effect.|
|Unique Paper ID: 147135|
Publication Volume & Issue: Volume 5, Issue 4
Page(s): 307 - 310
|Article Preview & Download|
Comprehensive Analysis of Energy Aware Clustering ...
Paper ID : IJIRT148784
A Practical Guide to live a Great Life in 2020 & b...
Paper ID : IJIRT148781
PERFORMANCE ANALYSIS OF LOAD BALANCING ALGORITHM I...
Paper ID : IJIRT148779
Review on various Face Artefact Detection mechanis...
Paper ID : IJIRT148778
Application of Six Sigma DMAIC Approach in Manufac...
Paper ID : IJIRT148777