Composites are widely used in many industries such as automobile, aeronautical, sports industry, civil engineering. The drop impact loads critical for aircraft composite components and damaged also produce unlimited defects or failure in the composites. The composites may be damaged due to tensile, compressive, impact force and shear stress on the composite parts. The composites may undergo in service damage due to dropping of tools, Runway debris in aircraft, hailstorm during flying of aircraft and hitting of birds and aircraft Due to drop impact damage the composite strength decreases drastically this will affects the load carrying capacity and the performance of the material. The finding the damage will not reduce the problem of failures but rectification and repairing may help saving the composite material and saving the lives using the composite material. Here and attempt is carried out to repair the impact damaged composite specimen and increasing strength of damaged composite. The repaired composite experimentally tested for the suitability for further use. The comparison of photo graphic images of good composite specimen and impact repair composite specimen were carried out.