Photoluminescence and Structural Study of Tb3+ doped Y2O3 Nanophosphor prepared by Homogenous Coprecipitation Method
Author(s):
Sanjay Rangnath Kale
Keywords:
Photoluminescence, homogenous coprecipitation, Y2O3:Tb3+
Abstract
Highly crystalline 1% to 5 % Tb3+ doped Y2O3 nanoparticle was synthesized by simple and cost effective homogenous coprecipitation method. Thus formed precipitate was dried at 100OC followed by calcination at 600OC for 2 hours and at 800OC for 2 hours. The cubic phase crystalline structure of Y2O3 and Y2O3:Tb3+ particles was confirmed by XRD analysis. The lattice parameter (d) and crystalline size (D) were found to be ~3.05 nm, and ~34.91 nm respectively. (JCPDS- 43-1036). The surface morphology with spherical particles, elemental analysis and composition of thus synthesized Y2O3:Tb3+ particles were proven by FESEM, EDX and FTIR investigations. Finally, the photoluminescence (PL) spectra shows one sharp and intense emission peak at 543 nm corresponding to 5D4 → 7F5 transition (bright green emission) of the phosphor particles.
Article Details
Unique Paper ID: 156582

Publication Volume & Issue: Volume 9, Issue 4

Page(s): 193 - 196
Article Preview & Download


Share This Article

Conference Alert

NCSST-2021

AICTE Sponsored National Conference on Smart Systems and Technologies

Last Date: 25th November 2021

SWEC- Management

LATEST INNOVATION’S AND FUTURE TRENDS IN MANAGEMENT

Last Date: 7th November 2021

Go To Issue



Call For Paper

Volume 8 Issue 4

Last Date 25 September 2021

About Us

IJIRT.org enables door in research by providing high quality research articles in open access market.

Send us any query related to your research on editor@ijirt.org

Social Media

Google Verified Reviews

Contact Details

Telephone:6351679790
Email: editor@ijirt.org
Website: ijirt.org

Policies